308L Stainless Steel Mig Wire
High quality 308LSi grade stainless steel MIG welding wire. A continuous solid corrosion resisting chromium-nickel wire for welding of austenitic chromium nickel alloys of 18% Cr - 8% Ni-type. 308LSi MIG WELDING WIRE has a good general corrosion resistance.
 
The alloy has a low carbon content which makes it particularly recommended where there is a risk of intergranular corrosion. The higher silicon content improves the welding properties such as wetting. The alloy is widely used in the chemical and food processing industries as well as for pipes, tubes and boilers. Welding current DC(+)

308L Stainless Steel Mig Wire

SKU: TR39-1612109820PESAB308L
£119.60Price
Size

  • Typical Tensile Properties

    Condition As Welded As Welded
    Shielding Gas   Tested at 350°C.
    Tensile Strength 570 MPa 490 MPa
    Yield Strength 400 MPa 370 MPa
    Elongation 36 % 25 %

    Deposition Data

    Current

    Deposition

    Rate

    		 Diameter Voltage

    Wire Feed

    Speed
    55-160 A 1.0-4.1 kg/h 0.8 mm 15-24 V

    1.0-4.1 m/min
    80-240 A 1.5-6.0 kg/h 1.0 mm 15-28 V 1.5-6.0 m/min
    100-300 A 1.6-7.5 kg/h 1.2 mm 15-29 V 1.6-7.5 m/min
    65-220 A 1.1-5.4 kg/h 0.9 mm 15-28 V 1.1-5.4 m/min
    0.0-0.0 kg/h 0.6 mm

    0.0-0.0m/min
    0.0-0.0 kg/h 1.14 mm 0.0-0.0 m/min
    230-375 A 5.2-8.6 kg/h 1.6 mm 23-29 V 5.2-8.6 m/min

    Classifications

    Wire Electrode SFA/AWS A5.9 : ER308LSi
    Werkstoffnummer : ~1.4316
    EN ISO 14343-A : G 19 9 L Si

    Approvals

    Grade 308L SA BT (M12)
    Society BV
    Approvals are based on factory location. Please contact ESAB for more information.

    Consumable Characteristics

    Alloy Type Austenitic (with approx. 8 % ferrite) 19% Cr - 9% Ni - Low C - High Si

    Typical Weld Metal Analysis %

    Wire

    Composition
    C Cr Cu Mn Mo Ni Si

    Si+Fe
    0.01 % 19.9 % 0.10 % 1.8 % 0.15 % 10.5 % 0.9 % 9 %